Loctite HY 4070
€26,10 – €72,25
Loctite 660 is designed for the bonding of cylindrical fitting parts, particularly where bond gaps can approach 0.50 mm (0.02 in.). The product cures when confined in the absence
of air between close fitting metal surfaces and prevents loosening and leakage from shock and vibration.
This product possesses excellent gap cure characteristics. Typical applications include restoring correct fits on worn shafts, spun bearings, and damaged keyways.
This product may vary on delivery times.
Minimum Order Quantity:
- 11 g: 12;
- 45 g: 6.
- Description
- Additional information
- Reviews (0)
- Technical Data Sheet
- Promotion
Description
NSF International
Registered to NSF Category P1 for use as a sealant where there is no possibilty of food contact in and around food processing areas. Note: This is a regional approval. Please contact your local Technical Service Center for more information and clarification.
TYPICAL PROPERTIES OF UNCURED MATERIAL
- Specific Gravity @ 25 °C 1.13
- Flash Point – See SDS
- Viscosity, Brookfield – HBT, 25 °C, mPa·s (cP):
- Spindle TB, speed 0.5 rpm, ,
Helipath 1,000,000 to 2,000,000LMS - Spindle TB, speed 5.0 rpm,
Helipath 150,000 to 350,000LMS
- Spindle TB, speed 0.5 rpm, ,
TYPICAL CURING PERFORMANCE
Cure Speed vs. Substrate
The rate of cure will depend on the substrate used. The graph below shows the shear strength developed with time on steel pins and collars compared to different materials and tested according to ISO 10123.
Cure Speed vs. Bond Gap
The rate of cure will depend on the bondline gap. The following graph shows shear strength developed with time on steel pins and collars at different controlled gaps and tested according to ISO 10123.
Cure Speed vs. Temperature
The rate of cure will depend on the temperature. The graph below shows the shear strength developed with time at different temperatures on steel pins and collars and tested according to ISO 10123.
Cure Speed vs. Activator
Where cure speed is unacceptably long, or large gaps are present, applying activator to the surface will improve cure speed. The graph below shows the shear strength developed with time on zinc dichromate steel pins and collars using Activator 7471™ and 7649™ and tested according to ISO 10123.
Additional information
| Weight | N/A |
|---|---|
| Technology | Cyanoacrylate / Acrylic Hybrid |
| Chemical Type | Cyanoacrylate, Methacrylate |
| Appearance (uncured) | Clear colorless to slightly yellow liquid, Transparent, cloudy, colorless to pale yellow |
| Fluorescence | No |
| Components | Two components – requires mixing |
| Viscosity | Non-sag |
| Mix Ratio by volume | 10 : 1 |
| Cure | Two component cure after mixing |
| Application | Bonding |
| Quantity | 11 g, 45 g |
| Brand | |
| EAN | 0079340011717 |
Only logged in customers who have purchased this product may leave a review.
Reviews
There are no reviews yet.